SLA 250/30 |
SLA 250/50 |
SLA 250/50HR |
| Laser |
Type
|
HeCd |
HeCd
|
HeCd |
|
Wavelength
|
325 nm |
325 nm
|
325 nm |
|
Power at vat (at 2000 hrs) |
12 mW |
24 mW
|
6 mW |
|
Warranty (one (1) year prorated) |
2000 hrs |
2000 hrs
|
2000 hrs |
|
| Recoating
System |
Process
|
Doctor
Blade |
Zephyr recoater
|
Zephyr recoater |
|
Min.
recommended layer thickness* |
0.15 mm (0.006 in) for
ACES™ and QuickCast™ build styles |
0.1 mm (0.004 in) for ACES and QuickCast build styles
|
0.0625 mm (0.0025 in) for
TECHWEAVE only** |
|
| Optical
& Scanning |
Spot
size (diameter @ 1/e˛)
|
0.20-0.28 mm (0.008- 0.011
in) |
0.20-0.28 mm (0.008- 0.011 in)
|
0.06- 0.08 mm (0.0025-
0.0035 in) |
|
Maximum
part drawing speed |
762 mm/sec (30 in/sec) |
762 mm/sec (30 in/sec)
|
635 mm/sec (25 in/sec) |
|
| Elevator |
Vertical
resolution
|
0.0025 mm (.0001 in) |
|
|
|
Maximum
part weight |
9.1kg (20lb) |
|
|
|
|
Vat Capacity |
Volume
|
32.2 L (8.5 US gal) |
|
|
|
Maximum
build envelope |
250 x 250 x 250 mm (10
x 10 x 10 in)** |
|
|
|
Interchangeable
vat |
No |
Yes
|
Yes |
|
| Software |
Operating
system
|
MS-DOS |
|
|
Network
type & protocol |
Ethernet, IEEE 802.3 using TCP/IP and
NFS |
|
|
|
Power (other options available) |
120
V AC ± 10%, 10A, 50/60 Hz or 230 V AC ± 10%, 5.2A, 50/60 Hz
|
|
| Ambient
Temperature |
Temperature
range
|
20-26°C (68-79°F) |
|
|
|
Maximum
change rate |
1°C/hour (1.8°F/hour) |
|
|
|
Relative
humidity |
Less than 50%, non-condensing |
|
|
|
|
Size |
Crated
|
W1.42 x D0.91
x H2.00 m (W56 x D36 x H79 in) |
|
Uncrated |
W1.24 x D0.69
x H1.64 m (W49 x D27 x H64.5 in) |
|
| Weight |
Crated
|
461 kg (1,014 lb) |
|
|
|
Uncrated
|
362 kg (796 lb) |
|
|
|
| Warranty |
One
(1) year including parts and labor. Laser under separate warranty.
|
|
|
QuickCast Compatibility |
Yes
|
|
|
|
|
|
*
Dependant upon part geometry, build parameters and material.
** For the SLA 250HR, optimal part building is obtained in a 5 x 5
in. square area about the center of the platform; this is especially
true as layer thickness is reduced toward the 0.0025 in. minimum layer
thickness.
|
|